849 SteelKote MC HB Midcoat

One component moisture cure high build polyurethane coating, reinforced with
micaceous iron oxide for application in high humidity (damp surface) and at low
temperatures. High performance/thin film technology. High quality mio pigmented
intermediate/sealer and coating on pre-treated steel. In combination with 849
SteelKote MC HB Primer it provides excellent tight and impenetrable protection in
aggressive environments. Ideal coating for maintenance jobs under humid and/or
cold weather conditions.

Product information

Features
• moisture cure technology;
• unique maintenance coating;
• all weather application;
• brush roll and spray application;
• high flexibility;
• curing at low temperatures;
• high mechanical strength;
• resistant to seawater, potable and sewage water, crude
• oil and various chemicals and solvents;
• short drying and curing cycles for fast processing;
• good brush application properties.

Performance and properties
Gloss: Matt
Volume solids: 58 volume % 
VOC: ≤ 380 gr/ltr.

Dry times
At 50% RH and at a standard dry film thickness of 80 μm.
(method: BYK Drying recorder)
Dust free 30 minutes
Manageable: 4 hours
Recoatable: 4 hours (max. 5 days)

Processing

Airless spray
Thinner PU5801
Quantity +/- 5 vol.%
Nozzle 0,019 inch 
Flow pressure min. 150 bar
Dry film thickness 80-100 µm

Airmix
Thinner PU5801
Quantity +/- 5 vol.%
Nozzle 0,019 inch
Flow pressure min. 80 bar
Dry film thickness 80-100 µm

Brush-roller
Thinner S5102 
Quantity 0-5 vol. %
Dry film thickness 40-60 µm

Airspray
Thinner PU5801
Quantity +/- 10 vol.%
Nozzle min 1,5 mm
Flow pressure min 3-4 bar
Dry film thickness 80-100 µm

Cleaning tools: Immediately after application using thinner PU5801.

Packaging

Packaging:

5 and 20 ltr cans and 200 litre drums. Thinner in 25 litre cans and 200 litre drums.

Shelf life:

In original well shut packaging 12 months, stored inside at temperatures between 5°C and 40°C.

Features
• moisture cure technology;
• unique maintenance coating;
• all weather application;
• brush roll and spray application;
• high flexibility;
• curing at low temperatures;
• high mechanical strength;
• resistant to seawater, potable and sewage water, crude
• oil and various chemicals and solvents;
• short drying and curing cycles for fast processing;
• good brush application properties.

Performance and properties
Gloss: Matt
Volume solids: 58 volume % 
VOC: ≤ 380 gr/ltr.

Dry times
At 50% RH and at a standard dry film thickness of 80 μm.
(method: BYK Drying recorder)
Dust free 30 minutes
Manageable: 4 hours
Recoatable: 4 hours (max. 5 days)

Airless spray
Thinner PU5801
Quantity +/- 5 vol.%
Nozzle 0,019 inch 
Flow pressure min. 150 bar
Dry film thickness 80-100 µm

Airmix
Thinner PU5801
Quantity +/- 5 vol.%
Nozzle 0,019 inch
Flow pressure min. 80 bar
Dry film thickness 80-100 µm

Brush-roller
Thinner S5102 
Quantity 0-5 vol. %
Dry film thickness 40-60 µm

Airspray
Thinner PU5801
Quantity +/- 10 vol.%
Nozzle min 1,5 mm
Flow pressure min 3-4 bar
Dry film thickness 80-100 µm

Cleaning tools: Immediately after application using thinner PU5801.

Packaging:

5 and 20 ltr cans and 200 litre drums. Thinner in 25 litre cans and 200 litre drums.

Shelf life:

In original well shut packaging 12 months, stored inside at temperatures between 5°C and 40°C.